Sintered Bronze Ames-A4@, type C-T8Z4-K140 according to UNE 96002:2006 standard
Sintered steel, type FOOC2-K200 according to ISO 5755:2012 standard
Sintered Bronze Ames-A4@, type C-T8Z4G-K120 according to UNE 96002:2006 standard
Sintered steel, type FOOC2-K200 according to ISO 5755:2012 standard
Oil
Mineral paraffin Ames-01: viscosity ISO VG 68
Mineral paraffin Ames-02, with higher load capacity at higher pressures or lower speeds, and improved start-stop behaviour
Maximum load (MPa)
Shaft speed (m/s)
Shaft speed (m/s)
Shaft speed (m/s)
Shaft speed (m/s)
< 0,25 or oscillating movement
0,25 - 0,50
0,50 - 5,00
< 0,25 or oscillating movement
0,25 - 0,50
0,50 - 5,00
< 0,25 or oscillating movement
0,25 - 0,50
0,50 - 5,00
< 0,25 or oscillating movement
0,25 - 0,50
0,50 - 5,00
10
3,5
2,5
8
3
2
12
4
2,5
12
3,5
2
Working temperature (ºC)
-20 to +120
Dimensional tolerances
Tolerances according to ISO 2795 standard (see tables of dimensions)
Properties
Typical
Minimum
Maximum
Typical
Minimum
Maximum
Typical
Minimum
Maximum
Typical
Minimum
Maximum
Density (g/cm3)
-
6,4
6,8
-
5,6
6,0
-
6,3
6,7
-
5,6
6,0
Oil content (%)
-
19
-
-
19
-
-
19
-
-
19
-
Total porosity (%)
22
-
-
22
-
-
22
-
-
22
-
-
Radial crushinf strength (MPa)
170
140
-
200
160
-
150
120
-
200
160
-
Hardness (HB)
35
-
-
40
-
-
30
-
-
40
-
-
SELFOIL®
Bronze
Iron
Material
Sintered Bronze Ames-A4@, type C-T8Z4-K140 according to UNE 96002:2006 standard
Sintered steel, type FOOC2-K200 according to ISO 5755:2012 standard
Oil
Mineral paraffin Ames-01: viscosity to ISO VG 68
Maximun load (MPa)
Shaft speed (m/s)
Shaft speed (m/s)
< 0,25 or oscillating movement
0,25 - 0,50
0,50 - 5,00
< 0,25 or oscillating movement
0,25 - 0,50
0,50 - 5,00
10
3,5
2,5
8
3
2
Working temperature (ºC)
-20 a +120
Dimensional tolerances
Tolerances according to ISO 2795 standard (see tables of dimensions)
Properties
Typical
Minimum
Maximun
Typical
Minimum
Maximun
Density (g/cm3)
-
6,4
6,8
-
5,6
6,0
Oil content (%)
-
19
-
-
19
-
Total porosity (%)
22
-
-
22
-
-
Radial crushing strength (MPa)
170
140
-
200
160
-
Hardness (HB)
35
-
-
40
-
-
SELFOIL® High Performance
Bronze
Iron
Material
Sintered Bronze Ames-A4@, type C-T8Z4G-K120 according to UNE 96002:2006 standard
Sintered steel, type FOOC2-K200 according to ISO 5755:2012 standard
Oil
Mineral paraffin Ames-02,with higher load capacity at higher pressures or lower speeds, and improved start-stop behaviour
Maximun load (MPa)
Shaft speed (m/s)
Shaft speed (m/s)
< 0,25 or oscillating movement
0,25 - 0,50
0,50 - 5,00
< 0,25 or oscillating movement
0,25 - 0,50
0,50 - 5,00
12
4
2,5
12
3,5
2
Working temperature (ºC)
-20 a +120
Dimensional tolerances
Tolerances according to ISO 2795 standard(see tables of dimensions)
Properties
Typical
Minimum
Maximum
Typical
Minimum
Maximun
Density (g/cm3)
-
6,3
6,7
-
5,6
6,0
Oil content (%)
-
19
-
-
19
-
Total porosity (%)
22
-
-
22
-
-
Radial crushing strength (MPa)
150
120
-
200
160
-
Hardness (HB)
30
-
-
40
-
-
NOTA: SELFOIL® High Performance data are for bearings with an inner diameter greater than 30 mm.
AMES can provide special materials and oils, suitable for the most demanding conditions of service. For further details please contact us via: www.ames-sintering.com.